N08926/No8926 is a nickel base alloy containing titanium and aluminum, containing enough chromium to form and maintain enough chromium oxide, so that it is protected under high temperature conditions, more resistant to high temperature than traditional chromium nickel stainless steel such as 304; The higher nickel content gives it better oxidation resistance than the standard 18-8 type rust, which is no less resistant to oxidation than the higher grade alloys with temperatures up to 1900 ° F (1038 ° C).
Email:info@tiscosteel.com
Email:anqi@jkxsteel.com
WhatsApp/WeChat/Mobile:+86-13563560199
Thickness |
0.3-200mm |
Length: |
2000mm, 2438mm, 3000mm, 5800mm, 6000mm,12000mm, etc |
Width |
40mm-600mm, 1000mm, 1219mm, 1500mm, 1800mm, 2000mm, 2500mm, 3000mm, 3500mm, etc |
Standard: |
ASTM,AISI,JIS,GB, DIN,EN |
Surface: |
BA,2B,NO.1,NO.4,4K,HL,8K |
Application: |
It is widely used in high-temperature and electric industry, medical devices, construction, chemistry, food industry, agriculture, and ship components. It also applies to food and beverage packaging, kitchen supplies, trains, aircraft, conveyor belts, vehicles, bolts, nuts, springs, and screen mesh etc. |
Certification: |
ISO, SGS,BV |
Technique: |
Cold Rolled Hot Rolled |
Edge: |
Mill Edge \ Slit Edge |
Grade (ASTM UNS) |
201,304,304L,321,316,316L,317L,347H,309S,310S,430,904L, S32205,2507,254SMOS,32760,253MA,N08926,etc |
序号 |
EN |
ASTM/UNS |
C |
N |
Cr |
Ni |
Mo |
成分 |
1 |
1.4301 |
304 |
0.04 |
|
18.1 |
8.3 |
|
|
2 |
1.4307 |
304L |
0.02 |
|
18.1 |
8.3 |
|
|
3 |
1.4541 |
321 |
0.04 |
|
17.3 |
9.1 |
|
Ti0.24 |
4 |
1.4550 |
347 |
0.05 |
|
17.5 |
9.5 |
|
Nb0.012 |
5 |
1.4401 |
316 S31608 |
0.04 |
|
17.2 |
10.2 |
2.1 |
|
6 |
1.4404 |
316L S31603 |
0.02 |
|
17.2 |
10.2 |
2.1 |
|
7 |
1.4406 |
316LN |
0.02 |
0.14 |
17.2 |
10.3 |
2.1 |
|
8 |
1.4429 |
S31653 |
0.02 |
0.14 |
17.3 |
12.5 |
2.6 |
|
9 |
1.4571 |
316Ti S31635 |
0.04 |
|
17 |
10.6 |
2.1 |
Ti0.30
|
10 |
1.4438 |
317L S31703 |
0.02 |
|
18.2 |
13.5 |
3.1 |
|